Al-Fe hypoeutectic alloys are a family of casting alloys characterized by cell growth, low cost and appreciable formability. It is well known that fatigue strength is a requirement of prime importance considering the nature of load typically observed during operations involving the risers used in oil extraction. The aim of this study is to examine the influence of cell size and its intercellular phase distribution on the fatigue life (Nf) of the directionally solidified Al-0.5, 1.0 and 1.5wt% Fe alloys. A water-cooled vertical upward unidirectional solidification system was used to provide the castings. Microscopy light and SEM microscopy were used. It was found that fatigue life decreases as cell spacing (λ c) increases. Smaller cell spacing allows a homogeneous distribution of Al-Fe fibers to happen within the intercellular regions, which tends to improve the mentioned fatigue property. Hall-Petch type correlations [Nf= Nf0+A(λc -1/2)-B(λc -1); where A and B are constants] seems to be able to encompass the fatigue life variation along the Al-Fe alloys.

Experiments were conducted to investigate the influence of thermal parameters on the columnar to equiaxed transition during the horizontal unsteady-state directional solidification of Al-Si alloys. The parameters analyzed include the heat transfer coefficients, growth rates, cooling rates, temperature gradients and composition. A combined theoretical and experimental approach is developed to determine the solidification thermal variables considered. The increasing solute content in Al-Si alloys was not found to affect significantly the experimental position of the CET which occurred for cooling rates in the range between 0.35 and 0.64 K/s for any of three alloy compositions examined. A comparative analysis between the results of this work and those from the literature proposed to analyze the CET during upward vertical solidification of Al-Si alloys is reported and the results have shown that the end of the columnar region during horizontal directional solidification is abbreviated as a result of about six times higher thermal gradient than that verified during upward unidirectional solidification of alloys investigated.